JOURNAL OF ALLOYS AND COMPOUNDS
卷 507, 期 1, 页码 215-224出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2010.07.160
关键词
Lead-free solders; Sn-Ag-Cu; Mechanical property; Microstructure; Strain rate
In this paper, the tensile tests were conducted at 25 degrees C to investigate the effect of Ag content and Ni doping on the microstructures and mechanical properties of Sn-3.0Ag-0.5Cu, Sn-2.0Ag-0.5Cu, Sn-1.0Ag-0.5Cu, Sn-1.0Ag-0.5Cu-0.05Ni and Sn-1.0Ag-0.5Cu-0.02Ni solders. The effect of strain rate on mechanical properties was investigated for each solder using stain rates of 10(-5) s(-1), 10(-4) s(-1), 10(-3) s(-1), 10(-2) s(-1) and 10(-1) s(-1). In addition, the effect of temperature on mechanical properties was investigated for Sn-1.0Ag-0.5Cu-0.02Ni solder by conducting tests at -35 degrees C, 25 degrees C, 75 degrees C and 125 degrees C. Test results show that the elastic modulus, yield stress and ultimate tensile strength increase with increasing strain rate and Ag content, but they decrease with increasing temperature. The elastic modulus, yield stress and ultimate tensile strength are lower and the elongation is larger for Sn-1.0Ag-0.5Cu-0.05Ni solder compared with Sn-1.0Ag-0.5Cu-0.02Ni solder. The strain rate and Ag content dependent mechanical property models have been developed for Sn-Ag-Cu solders for the first time. In addition, the temperature and rate-dependent mechanical property models have also been developed for Sn-1.0Ag-0.5Cu-0.02Ni solder. The microstructures of solders were also analyzed. The Ag content affects Ag3Sn intermetallic compound dispersion and Sn dendrite size. The microstructures of solder have fine Sn dendrites and more dispersed IMC particles for the high Ag content solder, which makes the solder exhibit high strength and yield stress. (C) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据