JOURNAL OF ALLOYS AND COMPOUNDS
卷 489, 期 1, 页码 125-129出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2009.09.030
关键词
Nano-structured mullite; Activated mechanically; Synthesis; Sintering; Microstructure; Phase transitions
Nano-structured mullite was produced from the microwave heating of a mixture of clay and alumina activated mechanically in a planetary ball mill for 30, 50 and 70 h. XRD results showed after 30 h milling time, clay disappeared and alumina and quartz appeared as the only crystalline phases. The maximum specific surface area was 34.92 m(2)/g for the sample activated mechanically for 30 h. The mullitization was completed for powders milled for 30 and 50 h and heated for 30 min (equal to 1376 degrees C) in a microwave oven. The maximum density and flexural strength values were measured for samples milled for 30 and 50 h, respectively, and sintered for 30 min. The flexural strength values of these samples were 3 and 4.7 times of the strength value of the sample milled for 2 h and sintered at the same conditions. (c) 2009 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据