期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 483, 期 1-2, 页码 389-393出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2008.08.107
关键词
CNT; Brake lining; Friction; Wear
Focus of this study has been placed on the influences of carbon nanotube (CNT) on the mechanical and tribological behavior of CNT containing brake lining materials. Different concentration of catalyst for growing CNT was dispersed into the commercial friction powder by sol-gel method before fed into the CVD process to fabricate the CNT friction powder. The CNT containing brake lining specimens were fabricated by hot pressing these homemade CNT containing friction powders. Experimental results indicate that the open porosity decreases and the bulk density of CNT containing brake lining specimens increases with the concentration of catalyst. Significant enhancement of specimen's hardness was obtained when the CNT containing friction powders are adopted by sot-gel catalyst dispersion and CVD process. The green (0 M concentration of catalyst) specimen which was fabricated by hot pressing commercial friction powders shows less stable, higher friction coefficient and larger mass loss during the wear test. On the contrary, the CNT containing brake lining specimens exhibit better performance, lower friction coefficients and lower mass loss. Morphological observations show that smooth, adherent lubricating films are formed on the sliding surface of CNT containing brake lining specimens, especially for specimens with high concentration of catalyst. Based on the experimental results, the CNT proves to be beneficial in improving the friction and wear performance of the brake lining materials. (C) 2008 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据