期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 468, 期 1-2, 页码 370-374出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2008.01.073
关键词
Ferroelectrics; Grain boundaries; Scanning and transmission electron microscopy; X-ray diffraction
资金
- Darfon Electronics Corps
The microstructures and electrical properties of the perovskite-type (Ba0.95 +/- xCa0.05)(Ti0.82Zr0.18)O-3 oxides with variousA/B ratios were Studied using X-ray diffraction (XRD) and transmission electron microscopy (TEM) with all energy-dispersive X-ray spectrometer(EDS). XRD results reveal that a second phase of Ba6Ti17O40 was formed when the A/B ratio was lower than 0.9956. TEM results show that liquid eutectic BaTiO3-Ba6Ti17O40 affects the sintering behavior and enhances grain growth; the grain size was significantly influenced when the A/B ratio changed from 0.9936 to 0.9976. The oxides' electrical performances in multilayer ceramic capacitors (MLCCs) with nickel electrodes were closely related to the A/B ratio of the powder. It was found that with decreasing A/B ratio, the maximum permittivity was increased due to a larger grain size, and the Curie point shifted to a higher temperature, which resulted in higher permittivity at room temperature. The highly accelerated life test (HALT) shows that reliability performance became worse with a decreasing A/B ratio due to the information of the second phase Ba6Ti17O40 at the grain boundary. (C) 2008 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据