期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 477, 期 1-2, 页码 764-767出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2008.10.131
关键词
Shape memory alloys; DC heating; Nickel-titanium; Arch wires; Mechanical property
资金
- National Key Scientific Program - Nanoscience and Nanotechnology [2007CB936103]
- National Research Foundation of Korea [220-2008-1-D00061] Funding Source: Korea Institute of Science & Technology Information (KISTI), National Science & Technology Information Service (NTIS)
The aim of this study was to investigate the effect of short-time DC heating on the phase transformation and superelasticity of a Ti-50.8at.%Ni alloy, which is extensively used as orthodontics arch wires. The alloy was pre-treated in three different conditions prior to the DC heating, including 15% cold-rolling (as-received), 15% cold-rolling and 673 K ageing (aged) and 15% cold-rolling and 973 K annealing (annealed). DC heating was performed using a Shinwa Bender Soarer-II equipment. DSC, XRD and tensile tests were employed to study the alloy's phase transformation behaviour, phase constituents, and superelasticity, respectively. It was found that the aged samples were sensitive to the short-time DC heating treatment and the dissolution of Ti3Ni4 precipitates into TiNi matrix completed within 15 s. In contrast, the as-received and the annealed samples showed little response to the DC heating. Such findings are of direct relevance to applications of TiNi as orthodontic arch wires, which often involve rapid electrical heating for shape setting. (c) 2008 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据