期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 467, 期 1-2, 页码 496-500出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2007.12.016
关键词
Ceramics; Thermoelectic materials; Sintering; Microstructure; Scanning electron microscopy
Synthesis of CuAlO2 and CuAl0.9Ca0.1O2 ceramics for thermoelectric application using a reaction-sintering process was investigated in this study. Without any calcination involved, the mixture of raw materials was pressed and sintered directly. Some peaks of remained Al2O3 were detected in CuAlO2. CaAl4O7 and CuO were detected in CuAl0.9Ca0.1O2. Density values 2.83-3.04 g/cm(3) were found in CuAlO2 pellets sintered at 1350 degrees C. In CuAl0.9Ca0.1O2 ceramics, density values 3.10-3.31 g/cm(3) were found in pellets sintered at 1350 degrees C. Thin polygonal grains were observed in CuAl0.9Ca0.1O2. The reaction-sintering process has proven a simple and effective method in preparing CuAlO2 and CuAl0.9Ca0.1O2 ceramics for thermoelectric application. (C) 2007 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据