TEOS; TFPS; sol-gel; superhydrophobicity; thermal stability; UV stability
资金
- National Science Foundation (NSF CMMI) [0422553]
- National Electric Energy Testing Research and Applications Center (NEETRAC) at Georgia Institute of Technology
Inorganic superhydrophobic, low-surface energy silica coatings have been prepared using sol-gel processing with tetraethoxysilane and trifluoropropyltrimethoxysilane as precursors. When trifluoropropyltrimethoxysilane was incorporated into silica, hydrophobic trifluoropropyl groups were present on the surface, yielding hydrophobicity. When combined with the rough surfaces from a sol-gel process, superhydrophobic surfaces can be generated. The surfaces were characterized by contact angle measurements, scanning electron microscopy and atomic force microscopy. Thermogravimetric analysis was used to determine the thermal stability of the as prepared silica materials. In order to measure the surface hydrophobicity retention of the silica surfaces under UV irradiation, UV accelerated aging tests were conducted according to ASTM D 4329. (c) Koninklijke Brill NV, Leiden, 2008
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据