JAPANESE JOURNAL OF APPLIED PHYSICS
卷 49, 期 9, 页码 -出版社
JAPAN SOC APPLIED PHYSICS
DOI: 10.1143/JJAP.49.09MD03
关键词
-
(Ca0.1Ba0.9)TiO3 + x wt % MnCO3 [x = 0, 0.2, 0.5, 1.0] (CBT-Mx) ceramics were prepared by conventional sintering, and their dielectric and piezoelectric properties were measured. The mechanical quality factor (Q(m)) of CBT was markedly enhanced by Mn addition and reached 2400 when x = 0.5. The dielectric loss tangent (tan delta) was 0.0023 at room temperature. The Curie temperature (T-C) was 133 degrees C. Then, the high power characteristics of CBT-M0.5 were investigated. The maximum vibration velocity (v(0)) of CBT-M0.5 was 1.1 m/s and was higher than that of Pb(Zr, Ti)O-3-based ceramics (Hard-PZT). The heat generation of CBT-M0.5 was smaller than that of Hard-PZT at the same v(0). The resonant frequency (f(r)) of CBT-M0.5 was stable up to v(0) of 1.1 m/s. Additionally, the temperature stability of fr was investigated in the practical application temperature range (from -20 to 80 degrees C). The amount of change in f(r) for CBT- M0.5 was larger than that for Hard-PZT below 10 degrees C. (C) 2010 The Japan Society of Applied Physics
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据