期刊
ISIJ INTERNATIONAL
卷 51, 期 8, 页码 1316-1321出版社
IRON STEEL INST JAPAN KEIDANREN KAIKAN
DOI: 10.2355/isijinternational.51.1316
关键词
blast furnace; softening-melting; high temperature properties; softening viscosity; melting reduction
To evaluate influences on the softening and melting behavior of blast furnace raw materials, the examinations of high temperature properties in various types of raw materials for blast furnaces were executed. Shrinking behavior before reaching approximately 1 300 degrees C is estimated by using softening viscosity taking into consideration pores of particles, and void ratio as well as liquid phase ratio of the layer. The softening viscosity of the solid phase of approximately 10(10) Pas was obtained and the influence of the mineral species of the solid phase or temperature is small. Melting reduction sharply progresses through expanding the liquid phase deriving from FeO and gangue. And this behavior is affected with position of the reduction curve and the liquidus curve. Sinter forms a solid phase from FeO and gangue due to a rise of reduction degree according to melting reduction. This solid obstructs contact of the liquid phase including FeO with coke, which restricts the progress of melting reduction. On the other hand, with lumpy ore and pellet, melting reduction rapidly progresses without interruption, since no solid phase is formed even when FeO decreases due to melting reduction.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据