IONICS
卷 20, 期 12, 页码 1767-1775出版社
SPRINGER HEIDELBERG
DOI: 10.1007/s11581-014-1136-x
关键词
Nickel-manganese hydroxide; Nickel-manganese-zinc hydroxide; Ball milling; Electrochemical property
In our previous study, Mn-substituted nickel hydroxide (Ni0.8Mn0.2(OH)(2)) was prepared by a simple ball milling method to reduce the cost of nickel hydroxide for alkaline secondary battery, but compared to the Ni(OH)(2) electrode, the Ni0.8Mn0.2(OH)(2) one showed an obvious decrease in its discharge potential. In this paper, Zn and Mn co-substituted nickel hydroxide (Ni0.8Mn0.2 -aEuro parts per thousand x Zn (x) (OH)(2), x = 0-0.075) is prepared by ball milling. The results of the cyclic voltammetry (CV) tests illustrate that the co-reduction of Mn(IV) to Mn(III) and NiOOH is observed on the Ni0.8Mn0.2 -aEuro parts per thousand x Zn (x) (OH)(2) electrodes, and it has a lower reduction potential than NiOOH. The co-substitution of Zn can effectively increase the co-reduction potential. The ball-milled Ni0.8Mn0.15Zn0.05(OH)(2) electrode has a similar capacity (about 270 mAh g(-1) at a 0.2C rate) and cycling durability to the commercial Ni(OH)(2) with ball milling treatment, but the former has better high-power performance.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据