XPS and ionic conductivity studies on Li1.3Al0.15Y0.15Ti1.7(PO4)3 ceramics

Li1.3Al0.15Y0.15Ti1.7(PO4)(3) compound was synthesized by solid-state reaction, and ceramics were sintered. The surfaces of the ceramics were investigated by scanning electron microscopy and X-ray photoelectron spectroscopy. Li1.3Al0.15Y0.15Ti1.7(PO4)(3) samples were tested in solid galvanic cells Ag|O-2+CO2|Li2CO3|Li1.3Al0.15Y0.15Ti1.7(PO4)(3)|LiMnO2+Mn2O3|O-2|Ag. The electromotive force measurements of this cell indicated that investigated samples are practically pure Li-ion conductors. Impedance spectroscopy studies have been performed in the frequency range 10(-2)-3 center dot 10(9) Hz and temperatures from -57 A degrees C to 334 A degrees C. Three dispersion regions related to Li+ ionic transport in bulk, grain boundaries of the ceramics and to polarization of electrodes have been found. Total conductivity changes according to Arrhenius law in the studied temperature range, but an anomalous behavior was observed for the bulk conductivity of the ceramics.