期刊
IONICS
卷 15, 期 1, 页码 107-110出版社
SPRINGER HEIDELBERG
DOI: 10.1007/s11581-008-0227-y
关键词
Supercapacitor; Zinc oxide; Carbon nanofoam; Specific capacitance
ZnCo2O4 nanomaterial was prepared by co-precipitation method and characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscopy (TEM), cyclic voltammetry (CV), and galvanostatic charge-discharge tests at various current densities. It is shown that the crystal structure and surface morphology play an important role in the enhancement of the specific capacitance. The TEM results clearly indicate that the prepared material shows aggregated particles. The particle size powder was about 50 nm, and SEM pictures indicate a porous morphology. The electrochemical behavior of ZnCo2O4 was characterized by mixing equal proportion of carbon nanofoam (CNF). From CV, it is concluded that the combination of redox and pseudo-capacitance increases the specific capacitance up to 77 F g(-1) at 5 mV s(-1) scan rate. The ZnCo2O4-based supercapacitor cell has good cyclic stability and high coulombic efficiency.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据