INTERNATIONAL JOURNAL OF NANOTECHNOLOGY
卷 10, 期 3-4, 页码 269-278出版社
INDERSCIENCE ENTERPRISES LTD
DOI: 10.1504/IJNT.2013.053140
关键词
Cu2Te; solar cell; superstrate; ball milling and printing
资金
- Innovative Solar Cells project (NEDO, Japan)
Cu2Te particles were synthesised by ball milling and then printed on an In2S3/TiO2/FTO-glass substrate, resulting in superstrate-structured solar cells. The as-prepared Cu2Te particles were amorphous, but their crystallinity was improved after annealing at 400-650 degrees C. The Cu2Te particles annealed at 400 degrees C, melted partially, and a completely melted Cu2Te film was obtained at annealing temperatures of 600-650 degrees C. The band gap of the Cu2Te films annealed at 400-600 degrees C was approximately 0.8 eV. The photovoltaic characteristics of the best full Cu2Te cells were as follows: short-circuit current, 21 mA/cm(2); open-circuit voltage, 0.24 V; fill factor, 0.3; and energy conversion efficiency, 1.57%. Thus, Cu2Te with its low melting point and high photocurrent is a promising candidate absorber layer for solar cell applications.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据