austenitic stainless steel; hot deformation; dynamic recrystallization; precipitation; activation energy
类别
资金
- Hamedan University of Technology [16.91.294]
Dynamic recrystallization and precipitation in a high manganese austenitic stainless steel were investigated by hot compression tests over temperatures of 950-1150 degrees C at strain rates of 0.001 s(-1)-1 s(-1). All the flow curves within the studied deformation regimes were typical of dynamic recrystallization. A window was constructed to determine the value of apparent activation energy as a function of strain rate and deformation temperature. The kinetics of dynamic recrystallization was analyzed using the Avrami kinetics equation. A range of apparent activation energy for hot deformation from 303 kJ/mol to 477 kJ/mol is obtained at different deformation regimes. Microscopic characterization confirms that under a certain deformation condition (medium Zener-Hollomon parameter (Z) values), dynamic recrystallization appears at first, but large particles can not inhibit the recrystallization. At low or high Z values, dynamic recrystallization may occur before dynamic precipitation and proceeds faster. In both cases, secondary phase precipitation is observed along prior austenite grain boundaries. Stress relaxation tests at the same deformation temperatures also confirm the possibility of dynamic precipitation. Unexpectedly, the Avrami's exponent value increases with the increase of Z value. It is associated with the priority of dynamic recrystallization to dynamic precipitation at higher Z values.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据