Palladium; Palladium oxide; Oxygen reduction reaction; Cathode; Solid oxide fuel cells
资金
- National Natural Science Foundation of China [U1134001, 51102079]
- National 863 project [2011AA050702]
Metallic Pd and PdO electrodes were prepared by using Pd and PdCl2 slurries, respectively, and their electrochemical performance as a cathode for oxygen reduction reaction in intermediate temperature solid oxide fuel cells was evaluated by electrochemical impedance spectroscopy (EIS) and direct current polarization (DC polarization). The electrochemical activity of metallic Pd was much higher than that of PdO for the reaction of oxygen reduction; below the decomposition temperature, a thin layer of PdO formed on the surface of metallic Pd electrode, which increased its polarization resistance. The decomposition temperature of PdO decreased from 810 to 750 degrees C as oxygen partial pressure decreased from 20 to 5 kPa, and was further lowered under the influence of the applied current during DC polarization test. The charge transfer resistance of PdO increased by decreasing oxygen partial pressure, while that of metallic Pd was less sensitive to it. Copyright (C) 2014, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据