Stainless steel; Hydrogen embrittlement; Prestrain; Low temperature
The effect of the prestrain at 80 K on hydrogen gas embrittlement (HGE) of Fe-Ni(10-16)-Cr17-mo2 alloys, based on type 316 stainless steel, was investigated in 1 MPa hydrogen and helium at 200 K. The HGE susceptibility of the alloy decreases with increasing prestrain and nickel equivalent, and no HGE is observed above the prestrain of 30% and the nickel equivalent of 27.2%. The fracture mode strongly depends on the prestrain and changes from the brittle transgranular fracture to the ductile dimple rupture with increasing prestrain. Prior strain induced alpha' martensite formed by the prestrain at 80 K does not show HGE, while dynamic strain induced alpha' martensite formed during the deformation after the prestrain shows HGE at 200 K. Copyright (C) 2013, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据