MICROPOROUS AND MESOPOROUS MATERIALS
卷 211, 期 -, 页码 147-151出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.micromeso.2015.03.003
关键词
High surface area; Mesoporous tungsten oxide; Tungsten nitride; Space-confined preparation
类别
资金
- Danish Council for Strategic Research [10-093906]
For the direct preparation of high surface area nitride materials, a lack of suitable precursors exists. Indirect preparation by gas phase nitridation (e.g. by ammonia) requires high temperatures and often results in sintering. The present work demonstrates that the space-confined preparation of W2N inside the pores of ordered mesoporous silica SBA-15 offers a possibility to reduce sintering phenomena and thus to obtain smaller particles, porous structures and a higher surface area material. The preparation was pursued in a two-step approach. First, WO3 was introduced into the channels of SBA-15 and second, ammonolysis was conducted for its conversion to W2N. When performed in the presence of the exo-template, SBA-15 acts as a stabilizer and small W2N particles (6-7 nm) with a high specific surface area (40 m(2) g(-1)) are obtained after template removal. When the template is, however, removed before nitridation, it cannot stabilize the W2N particles and enhanced sintering occurs. (C) 2015 Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据