Solid oxide electrolysis cell; Strontium-doped lanthanum manganite; Anode-electrolyte interface; Delamination; Lanthanum zirconate
资金
- ConocoPhillips
- Idaho National Laboratory
Symmetric cells of the configuration air/LSM//YSZ//LSM/air have been fabricated and electrically tested under impressed voltage conditions to understand the anode delamination behavior commonly observed during the operation of solid oxide electrolysis cells (SOEC). Electrical performance degradation has been measured with time at various applied voltages ranging from 0 to 0.8 V with respect to OCV, and cell component microstructural and chemical changes have been examined. Post-test observations indicate the development of a weak anode-electrolyte interface leading to the delamination of the anode from the electrolyte surface. Microstructural analysis of the anode-electrolyte interface revealed extensive morphological and chemical changes including the formation of lanthanum zirconate, an uneven porous interface, and localized grain boundary porosity in the electrolyte. An anode delamination mechanism based on morphological change and compound formation at the anode-electrolyte interface is proposed. Copyright (c) 2012, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据