INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
卷 37, 期 4, 页码 3056-3065出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.ijhydene.2011.11.041
关键词
Silver nanoparticles; Transient time; Photocurrent density; Hydrogen generation
资金
- Research and Technology Council of Sharif University of Technology
TiO2 thin films containing different concentrations of Ag nanoparticles have been synthesized by sol-gel method. According to UV-visible spectra, presence of an intense surface plasmon resonance peak at 490 nm of wavelength indicated formation of silver nanoparticles in the TiO2 films. Based on atomic force microscopy (AFM) analysis, the surface roughness and the effective surface ratio increased by increasing the Ag mol%. Moreover, scanning electron microscopy (SEM) images showed formation of Ag nanoparticles on the surface for the samples containing high Ag concentration. X-ray diffraction (XRD) patterns revealed that the size of Ag nanocrystals increased by increasing the Ag content in the films while the nanocrystalline size of TiO2 reduced in the presence of silver nanoparticles. Based on x-ray photoelectron spectroscopy (XPS) data, a stoichiometric chemical composition was detected for TiO2 while, Ag presented in a combination a metal/oxide states on the surface. Studying photoresponse of the samples showed that the highest photocurrent was obtained for the sample containing 1 mol% Ag. By measuring the photovoltage versus time, it was found that addition of silver nanoparticles to the TiO2 layer resulted in reduction of the transient time of the photogenerated carriers in the samples. Impedance spectroscopy determined a slight decrease in charge transfer resistance by addition of Ag to the films. Moreover, measuring the amount of hydrogen produced during water splitting reactions verified that the highest quantum yield of 9.6% was obtained for the sample with 1 mol% Ag. Copyright (C) 2011, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据