Hydrogen storage; Activated carbon; KOH activation; Synthesis conditions impact
资金
- CPER Structuration du Pole de Competitivite Fibres Grand'Est (Competitiveness Fibre Cluster), through local (Conseil General des Vosges)
- regional (Region Lorraine)
- national (DRRT and FNADT)
- European (FEDER) funds
39 activated carbons (ACs) were prepared by KOH activation of anthracite, using weight ratios KOH/anthracite (W) ranging from 1.5 to 7, activation temperatures (T) from 973 to 1073 K, and heating rates (Hr) from 1 to 5 K min(-1). ACs with high apparent surface areas (>3400 m(2) g(-1)), high micropore volumes (>1 cm(3) g(-1)) and high hydrogen storage capacities (up to 6.6 wt. %) were obtained. A statistical study was carried out to clarify the impact of synthesis conditions on hydrogen storage capacities of the resultant ACs. Analysis of variance (ANOvA) showed that both w and T have a significant impact on hydrogen storage capacity, whereas HT has not. A quadratic model was used to correlate W-2, W, T-2 and T to hydrogen storage capacities. The model adequately evaluated the impact of synthesis conditions on hydrogen storage capacities of the resultant ACs. Copyright (C) 2012, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据