INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
卷 36, 期 14, 页码 8604-8609出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.ijhydene.2011.04.017
关键词
Hydrogen storage alloy; Combustion synthesis; LaNi5; Calcio-thermic reduction; Gas-solid reaction; Activation treatment
资金
- Ministry of the Environment, Japan
- Grants-in-Aid for Scientific Research [21360476, 11J03412, 23656597] Funding Source: KAKEN
In this paper, we describe the self-ignition combustion synthesis (SICS) of LaNi5 utilizing the hydrogenation heat of metallic calcium at different hydrogen pressures, and focus on the effect of hydrogen pressure on the ignition temperature and the initial activation of hydrogenation. In the experiments, La2O3, Ni, and Ca were dry-mixed, and then heated at 0.1, 0.5, and 1.0 MPa of hydrogen pressure until ignition due to the hydrogenation of calcium. The products were recovered after natural cooling for 2 h. The results showed that the ignition temperature lowered with hydrogen pressure. The products changed from bulk to powder with hydrogen pressure. This was probably caused by volume expansion due to hydrogenation at higher pressure. The product obtained at 1.0 MPa showed the highest hydrogen storage capacity under an initial hydrogen pressure of 0.95 MPa. The results of this research can be applied as an innovative production route for LaNi5 without the conventional melting of La and Ni. Copyright (C) 2011, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据