期刊
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
卷 36, 期 11, 页码 6744-6750出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.ijhydene.2011.03.072
关键词
Mg-Pd-Ni ternary alloys; Mechanical alloying; Electrochemical hydrogen storage
资金
- The Scientific and Technological Research Council of Turkey [MAG 109M086]
Mg1-xPdxNi (x = 0.03, 0.05, 0.06, 0.07, 0.08, 0.10, 0.20) type alloys were synthesized by mechanical alloying and their electrochemical hydrogen storage characteristics were investigated. The XRD studies showed that Mg6Pd and Mg-Pd phases form in the high-Pd-containing alloys. The discharge capacities of the alloys increased sharply up to 15 h milling. Further increase up to 25 h did not cause change in the discharge capacities considerably. Among the Mg1-xPdxNi ternary alloys, Mg0.93Pd0.07Ni alloy was observed to exhibit the best charge/discharge cyclic performance. The hydrogen storage capacity of the high-Pd-containing alloys (Mg1-xPdxNi; x > 0.07) deteriorated as Pd content of the alloy increased. This observation was attributed to the Mg-Pd phase formations. According to the EIS experiments as Pd atomic ratio increased up to 0.07 the charge transfer resistances of the alloys decreased. Further increase in Pd atomic ratio, however, brought about the increase in the charge transfer resistances. Copyright (C) 2011, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据