INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
卷 34, 期 16, 页码 6852-6860出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.ijhydene.2009.05.138
关键词
Strontium-doped praseodymium; cobalt ferrites (PSCF); Oxygen reduction reaction; Gas diffusion; Area specific resistance; Power density
The electrochemical properties and microstructure changes of Pr0.3Sr0.7Co0.3Fe0.7O3-delta (PSCF3737) were studied in this paper. It was confirmed through X-ray photoelectron spectroscopy and extended X-ray absorption fine structure analysis that the oxygen vacancy of PSCF3737 was lower and that the atomic distance between an oxygen atom and a neighboring atom (especially cobalt) of PSCF3737 was longer compared to those of Pr0.3Sr0.7CoO3-delta (PSC37). In addition, the surface reaction of PSCF3737 changed from a one-electron reduction mechanism to a two-electron reduction mechanism, which may lead to enhancement of the cathode performance. The area specific resistance of PSCF3737 was 0.11 Omega cm(2) at 700 degrees C after changing the fabrication conditions of the cathode in order to optimize the microstructure. A single cell test was performed using PSCF3737. A maximum power density of 315 mW/cm(2) at 575 degrees C was obtained. Published by Elsevier Ltd on behalf of international Association for Hydrogen Energy.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据