INTERNATIONAL JOURNAL OF FATIGUE
卷 58, 期 -, 页码 144-151出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ijfatigue.2013.02.023
关键词
Very-high-cycle fatigue; Fatigue life; FGA; Crack extension rate; High strength steels
资金
- National Natural Science Foundation of China [11172304, 11021262, 11202210]
- National Basic Research Program of China [2012CB937500]
Fatigue tests of a high carbon chromium steel were performed using rotating bending and ultrasonic axial cycling. Fatigue crack initiated at specimen interior for very-high-cycle fatigue (VHCF) with fish-eye pattern embracing fine-granular-area (FGA) originated from inclusion. The fatigue life from FGA to fish-eye and from fish-eye to the critical crack size was respectively calculated, so as to estimate the fatigue life contributed by FGA. The crack extension rate within FGA was also estimated. Our results demonstrated that the formation of FGA is responsible for a majority part of total fatigue life. (C) 2013 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据