期刊
INTERNATIONAL JOURNAL OF FATIGUE
卷 48, 期 -, 页码 156-164出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ijfatigue.2012.10.015
关键词
Corrosion fatigue; AISI 4340 steel; Loading frequency; Stress ratio; Environmental effect
资金
- Office of Naval Research [N00014-08-1-0646]
- National Natural Science Foundation of China (NSFC) [10772115, 10932007]
Corrosion fatigue crack growth (CFCG) experiments of AISI 4340 high strength steel were conducted using pre-cracked compact tension specimens in dry air, distilled water, and 3.5% NaCl aqueous solution at different R-ratios (where R is the ratio of the minimum load over the maximum load in a loading cycle) and different loading frequencies. The material displays typical Type B CFCG behavior: significant environmental effect when the maximum stress intensity factor is above K-ISCC (the threshold stress intensity for stress corrosion cracking) and minimal environmental effect when the applied load is below the threshold value or above a large stress intensity factor. A new engineering model was developed to consider the interaction and competition between fatigue and environmental contributions. The R-ratio effect was considered using the Walker's equation. The baseline data required for the model is the data from stress corrosion in a given environment and the data from crack growth of the material in thy air or inert environment. The new model was found to correlate very well the CFCG experiments of AISI 4340 steel. (C) 2012 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据