Spot friction weld; Friction stir spot weld; Stress intensity factor; Fatigue; Cross-tension specimen
资金
- National Science Council [96-2221-E-194-047, 97-2221-E-194-014, 98-2221-E-194-007-MY3]
Failure modes of spot friction welds (SFWs) in cross-tension specimens of aluminum 6061-T6 sheets are investigated. Micrographs of the SFWs before and after failure under quasi-static and cyclic loading conditions are examined. Two different nugget pullout failure modes can be seen. A fatigue crack growth model based on the paths of the dominant kinked fatigue cracks is adopted to estimate the fatigue lives of SFWs. The computational stress intensity factors for finite kinked cracks and the Paris law for fatigue crack propagation are considered. The fatigue life estimations based on this model agree well with the experimental results. (C) 2011 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据