The present work is focused on the microstructural evolution of major components of carbonaceous samples during high temperature treatment, i.e. vitrinite in raw anthracites and dense particles in the heated samples. Three anthracites from distinct geological settings, with an Rr of 2.62%, 5.23%, and 6.25% (PBEB, ACB, and DB, respectively) were chosen for this research. The raw samples were previously carbonized at 1000 degrees C, and then subjected to high temperature treatment (HTT) at 1500, 2000, and 2500 degrees C, in a graphite furnace. From the results obtained by optical microscopy (RIS parameters), micro-Raman spectroscopy, and X-ray diffraction, it was possible to evaluate the subsequent structural and microtextural evolution of the heat treated materials. It was found that, during the carbonization process up to 1500 degrees C, the transformations are essentially of a chemical nature and are expressed by chemical and optical parameters (RIS main axes and R(ev) parameter). The magnitude of these changes is higher for the lower rank heat treated anthracite (PBEBC series). The structural order parameters obtained by X-ray diffraction show an increase in disorder at 1000 degrees C and a slight improvement after heat treatment at 1500 degrees C. The G band FWHM (cm(-1)) exhibits the same tendency at 1000 degrees C. However, due to the small size of the crystallites, this Raman parameter continues to increase at 1500 degrees C. After 2000 degrees C, there is an increase in the structural order in the materials of the heat treated samples. A three-dimensional ordering was observed in the materials of the DBC carbonized anthracite at 2500 degrees C, as exhibited by the X-ray diffraction parameters and Raman spectral features. The PBEBC and ACBC carbonized anthracites still retain their turbostratic structure after heat treatment at 2500 degrees C. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据