Processing and properties of polycrystalline cubic boron nitride reinforced by SiC whiskers

出版社

WILEY
DOI: 10.1111/ijac.13077

关键词

high-temperature high-pressure sintering; mechanical properties; polycrystalline cubic boron nitride; SiC whisker

资金

  1. Natural Science Foundation of Henan Province [162300410242]
  2. National Natural Science Foundation of China [51772275]

向作者/读者索取更多资源

Dense polycrystalline cBN (PcBN)-SiCw composites were fabricated by a two-step method: First, SiO2 was coated on the surface of cubic boron nitride (cBN) particles by the sol-gel method. Then, silicon carbide whisker (SiCw)- coated cBN powder was prepared by carbon thermal reaction between SiO2 and carbon powders at 1500 degrees C for 2 hour. Then, cBN-SiCw complex powders were sintered by high-pressure and high-temperature sintering technology using Al, B, and C as sintering additives. The phase compositions and microstructures of cBN-SiCw composites were investigated by X-ray diffraction and scanning electron microscopy, respectively. It was found that the SiCw and Al3BC3 had been fabricated by in situ reaction, which cannot only promote densification but also improve mechanical properties. The relative density of PcBN composites increased from 96.3% to 99.4% with increasing SiCw contents from 5 to 20 wt%. Meanwhile, the Vickers hardness, fracture toughness and flexural strength of as-obtained composites exhibited a similar trend as that of relative density. The composite contained 20 wt% of SiCw exhibited the highest Vickers hardness and fracture toughness of 42.7 +/- 1.9 GPa and 6.52 +/- 0.21 MPa center dot m(1/2), respectively. At the same time, the flexural strength reached 406 +/- 21 MPa.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.5
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据