INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY
卷 48, 期 5-8, 页码 597-605出版社
SPRINGER LONDON LTD
DOI: 10.1007/s00170-009-2304-4
关键词
Rapid manufacturing; Selective laser melting; W-Cu; Microstructure; Surface morphology
资金
- National High-Tech Program (863) of China [2007AA03Z115]
- Huazhong University of Science and Technology (HUST)
- Central South University of China [2008112022]
Tungsten-Copper (W-Cu) alloys are promising materials for electrical and thermal applications. However, its forming method still remains limited in conventional powder metallurgy technique which is not suitable for manufacturing parts with intricate shapes. In this work, selective laser melting technology was introduced for fabricating W-10 wt.% Cu alloys parts. The morphological feature of a single molten track was analyzed. The results show that liquid phase sintering with complete melting of the binder (Cu), but nonmelting of the structural metal (W), acts as the main mechanism in this process. The melting conditions of single layers in different processing parameters were investigated. The results show that a moderate melting zone can be acquired from an established process map. Moreover, investigations on multilayers forming show that the final density increases with the decrease of scan speed until it reaches a plateau due to the insufficient rearrangement in liquid phase sintering and the balling effect.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据