期刊
INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES
卷 31, 期 8, 页码 795-804出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ijadhadh.2011.07.008
关键词
Polyurethane; Dynamic mechanical analysis; Infrared spectra; Microscopy
资金
- Spanish Research Agency MICINN [MAT2010-19904]
- University of Alicante
Precipitated calcium carbonate filler (PCC) was added to a thermoplastic polyurethane adhesive (TPU). The addition of PCC produced a moderate increase in the rheological and viscoelastic properties of TPU due to the poor dispersion of filler (i.e. found to be clusters) and the weak interactions between the PCC nanoparticles and the polymer chains. The interactions were noticed by ATR-IR spectroscopy by displacement of the bands at 3326, 1729 and 1061 cm(-1) to higher wave number of the polyurethane. Furthermore, the first glass transition temperature of the polyurethane was found to decrease by adding PCC filler. The crystallinity of the soft segments in the TPU was decreased by adding PCC because of the disruption of the degree of phase separation in the polymer. The initial adhesive strength in PVC/TPU adhesive/PVC joints increased noticeably by adding PCC filler, the greater the amount of filler in the TPU, the greater the initial adhesive strength found. Finally, the highest final adhesive strength (72 h after joint formation) was obtained in the joint produced with the TPU containing 10 wt% PCC. (C) 2011 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据