期刊
INTERMETALLICS
卷 26, 期 -, 页码 78-85出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.intermet.2012.03.047
关键词
Intermetallics; Phase transformation; Joining; Diffraction; Environmental applications
资金
- Queensland Government, Australia
- [AS101/PD2249]
- [AS111/PD3364]
The crystallography of the Cu6Sn5 intermetallic that forms at the solder substrate interface in many soldering operations can be influenced by Ni additions. It has been established that when Ni is present at 5-9 at%, the high-temperature hexagonal Cu6Sn5 (eta) .does not transition to the low-temperature monoclinic Cu6Sn5 (eta') at the equilibrium temperature of 186 degrees C. In fact, the hexagonal phase remains stable from room temperature to 250 degrees C. This paper shows the stabilising effect of Ni exists in the range of 4.6-17.2 at% Ni in stoichiometric samples, over the larger temperature range of -100 to 250 degrees C using synchrotron X-ray diffraction. The results are also used in combination with dilatometry experiments and show that Ni decreases the magnitude of thermal expansion, and prevents the discontinuity in expansion that occurs with the polymorphic transformation. (C) 2012 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据