INTERMETALLICS
卷 22, 期 -, 页码 77-83出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.intermet.2011.10.006
关键词
Titanium aluminides; based on TiAl; Environmental embrittlement; Diffusion; Surface properties; Microprobe; Atom probe
资金
- NSF-MRI [DMR-0420532]
- ONR-DURIP [N00014-0400798, N00014-0610539, N00014-0910781]
Exposure of a Ti-45Al-5Nb alloy to elevated temperatures has been shown to result in a loss of ductility resulting from a near surface effect involving diffusion of oxygen into the alloy. Local electrode atom probe analysis was conducted at 2, 13, and 25 gm distance from the oxide/base-metal interface. Oxygen was preferentially located in the alpha(2) phase with concentrations up to 14.8 at.% and diminishing with increasing distance from the surface. Near surface microstructural changes were only visible up to 10 mu m from the surface but the oxygen diffusion significantly exceeded that distance. The diffusion coefficient of oxygen into the alpha(2) phase was estimated based on the oxygen concentrations obtained from local electrode atom probe analysis. Fluorine ion implantation on the surface was investigated as a possible solution to the embrittlement. Published by Elsevier Ltd.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据