Titanium aluminides, based on TiAl; Isothermal forging; Microstructure; Mechanical properties at ambient temperature; Mechanical properties at high temperatures
资金
- National Basic Research Program of China [2011CB605502]
- National Natural Science Foundation of China [51001040]
A new beta gamma TiAl alloy Ti-43Al-4Nb-2Mo-0.5B (at %) was fabricated by ISM method. The as-cast microstructure consisted of fine lamellar colonies and mixtures of small gamma and B2 grains around lamellar colony boundaries. By canned hot forging, the cast microstructure was further refined and homogenized. Microstructure evolution during hot forging was characterized by means of SEM, TEM and EBSD in detail. DRX and phase transformation during forging are also discussed; Based on nano-indentation tests, B2 was found much harder than gamma and alpha(2) phases. The tensile properties of the forged alloy were investigated and compared with as-cast condition; this forged alloy maintains high tensile strength over 900 MPa up to 750 degrees C, and tensile superplasticity appears above 800 degrees C. B2 phase is proved to be detrimental to room-temperature ductility and to reduce tensile strength sharply above 800 degrees C, mainly because of its hard and brittle nature at low temperature and its soft feature at high temperature. Crown Copyright (C) 2012 Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据