Iron aluminides (based on FeAl); Phase identification; Casting; Metallographic techniques
资金
- FAPESP (The Scientific Research Foundation of the State of Sao Paulo, Brazil)
- CNPq (The Brazilian Research Council)
- FAEPEX - UNICAMP
During the non-equilibrium solidification typical of DC (direct chill) castings a range of cooling rates occur from the surface to the casting center, and can cause the formation of metastable intermetallic phases (AlmFe, Al6Fe, etc.) in addition to the stable Al3Fe phase. The extensive presence of the plate-like Al3Fe phase in the as-cast structure adversely influences the mechanical properties of Al-Fe alloys, since this morphology is more likely to induce microcracks than the fibrous Al6Fe phase. The aim of this study was to present a method of characterization of AlFe intermetallics which is based on the dissolution of the aluminum matrix in distilled I-butanol. Optical microscopy and SEM analysis of the undissolved intermetallics have permitted characterization of the morphology, distribution, size and chemical composition of both Al3Fe and Al6Fe phases. The results have shown that Al6Fe prevails for growth rates V-L and cooling rates (T) over dot(L) higher than 0.7 mm/s and 1.5 K/s, respectively. (C) 2009 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据