EBSD; Mechanical characterization; High entropy alloys; Thermomechanical processing; Recrystallization; Shear bands
类别
资金
- Russian Scientific Foundation [14-19-01104]
- Russian Science Foundation [14-19-01104] Funding Source: Russian Science Foundation
Microstructure evolution in high-entropy alloy CoCrFeNiMn during uniaxial compression to a height reduction of true strain of approximate to 1.4 in the temperature interval 600-1100 degrees C was studied. Although some differences was observed in the mechanical behavior of the alloy and the activation energy of deformation in warm (below 800 degrees C) and hot (above 800 degrees C) temperature intervals, microstructure evolution at all studied temperatures was found to be accompanied by discontinuous dynamic recrystallization (dDRX). During hot deformation recrystallization was primary associated with nucleation of new grains on the initial grain boundaries, while in the warm interval dDRX was mainly observed in shear bands. The volume fraction of the recrystallized structure was respectively 0.085 and 0.95 at 600 and 1000 degrees C and the recrystallized grain size was found to be 0.2 and 40.4 mu m for 600 and 1100 degrees C, respectively. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据