期刊
出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2015.09.008
关键词
Medium Mn steel; Toughness; Reversed transformation austenite; Phase stability; Heavy plate
类别
资金
- National High-tech R&D Program (863 Program) [2015AA03A501]
- Department of Metallurgical and Materials Engineering, University of Texas at El Paso, USA
We elucidate structure-property relationship in a 0.1C-5Mn-0.4Mo hot rolled steel that was directly water-quenched and intercritically tempered at 650 degrees C. Tempering in the intercritical region for optimum time was critical in obtaining elongation of 25.0% and reduction in area of 65.4%. Moreover, the tensile strength was 875 MPa and the impact energy at test temperature of -60 degrees C was significantly high at 165.3J. The microstructure of water-quenched steel consisted of lath martensite, needle-shaped cementite, and about 1% retained austenite. The superior combination of strength, ductility, and toughness subjected to tempering for optimal time of 30 min is attributed to the dissolution of cementite, recovery of martensitic structure, and formation of approximately 13% reversed austenite with appropriate mechanical stability. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据