Long period stacking ordered (LPSO); Mg-Y-Ni-Ti alloy; Microstructure; Mechanical properties; Hot rolling
类别
资金
- National Natural Science Foundation of China [50571073, 51574175, 51474153]
- Ph.D. Programs Foundation of Ministry of Education of China [20111402110004]
- Natural Science Foundation of Shanxi Province [2009011028-3, 2012011022-1]
The microstructure evolution of Mg96Y3Ni1 alloy with different Ti contents were investigated. Mg95.8Y3Ni1Ti0.2 alloy achieved finest grains, which was composed of alpha-Mg and long period stacking ordered phase. The ultimate tensile strength of Mg95.8Y3Ni1Ti0.2 alloy reached to 435 MPa with elongation of 21% after hot rolling and aging treatment. (C) 2015 Elsevier B.V. All rights reserved.