Mg-5Sn alloy; Li addition; Mechanical properties; Fracture mechanism
类别
资金
- Ministry of Science and Technology of the PRC [2008DFR50040-08]
- sharing fund for Chongqing University's large-scale equipment [2011121511]
This work explores trace addition of Li on the magnesium alloy Mg-5Sn, with an emphasis laid on the microstructure, mechanical properties and fracture mechanism. The results reveal that with trace addition of Li, a new Li2MgSn phase forms distributed along the grain boundaries. When the concentration of Li increases, the secondary dendrite arm spacing of the primary alpha-Mg phase can be refined and the formation of Li2MgSn becomes more favored, and even totally substitute Mg2Sn phase finally. Trace addition of Li can significantly increase the yield stress and elongation to failure of Mg-5Sn alloy during both tensile and compressive tests, and manifests the highest ultimate strengthening effect during compression. The optimal comprehensive mechanical property is achieved in Mg-5Sn-0.3Li, with an ultimate compressive strength of 334 MPa. With the increment of Li, the fracture mechanism shifts from mixture of cleavage fracture and dimple fracture in Mg-5Sn alloy to the mechanism of cleavage fracture in Mg-5Sn-0.3Li and Mg-5Sn-1Li alloy. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据