期刊
出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2015.07.007
关键词
Work-hardening (WH); Dynamic-softening (DS); Hot deformation; Dislocation; Microstructural mechanism; GH4720Li superalloys
类别
资金
- National Natural Science Foundation of China [51101119]
- China Postdoctoral Science Foundation [2015M570851]
- University Innovation Research and Training Program of NPU [201510699058]
- Hong Kong Scholar Program [XJ2014047]
Competition between work-hardening effect and dynamic-softening behavior of as-cast GH4720Li superalloys with original dendrite microstructure during moderate-speed deformation was quantitatively investigated in this present paper. Flow behavior for processing the studied alloys with dendrite microstructure behaves typical three stages, caused by the competition effect between work-hardening and dynamic-softening. The relationships between work-hardening rate and true strain and true stress were derived from Kocks-Mecking dislocation relation. The work-hardening effect shows two obvious stages with strain, viz, steady fluctuations and linear decreasing. An obvious work-hardening effect was demonstrated under lower temperature and higher strain rate. The linear relationship of work-hardening rate theta on true stress epsilon was constructed with the slope only related to annihilation coefficient Omega. The microstructural mechanism of as-cast GH4720Li superalloys during moderate-speed deformation was referred to dislocation multiplication and dendrite fragmentation, and the latter was beneficial to dynamic recrystallization during moderate-speed deformation. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据