Microstructures and tensile properties of Al-2024 matrix composite containing 10 wt% Al4Sr intermetallic have been studied after extrusion process and T6 heat treatment. Microstructural examinations were assessed by the use of optical microscopy, scanning electron microscopy (SEM) and X-ray diffractometry. The results showed that changing the matrix from Al to 2024 alloy reduces the length of primary Al4Sr particles and improves ultimate tensile CUTS) values considerably from 206 MPa to 321 MPa which is based on the formation of Cu-rich intermetallics. Applying extrusion process and 16 heat treatment was found to be very effective in enhancing tensile properties of Al/2024-10Al(4)Sr composite. In current research, UTS and elongation values were found to be 381 MPa and 13.6%, introducing a tough composite. Moreover, the study of fracture surfaces of the hot-extruded composites specimens revealed that ductile mode of fracture is dominant. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据