A multiferroic BiFeO3 film was fabricated on a Pt/Ti/SiO2/Si(100) substrate by a chemical solution deposition (CSD) method, and this was followed by postdeposition annealing at 923 K for 10 min in air. X-ray diffraction analysis indicated the formation of the polycrystalline single phase of the BiFeO3 film. A high remanent polarization of 89 mu C/cm(2) was observed at 90 K together with a relatively low electric coercive field of 0.32 MV/cm, although the ferroelectric hysteresis loops could not be observed at room temperature due to a high leakage current density. The temperature dependence of the ferroelectric hysteresis loops indicated that these hysteresis loops lose their shape above 165 K, and the nominal remanent polarization drastically increased due to the leakage current. Magnetic measurements indicated that the saturation magnetization was less than 1 emu/cm(3) at room temperature and increased to approximately 2 emu/cm(3) at 100 K, although the spontaneous magnetization could not appear. The magnetization curves of polycrystalline BiFeO3 film were nonlinear at both temperatures, which is different with BiFeO3 single crystal.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据