DOI: 10.1016/j.msea.2014.09.047
关键词
Q&P process; Retained austenite; Product of strength and elongation; Work hardening behavior; TRIP effect; Fracture morphology
类别
资金
- National Natural Science Foundation of China [51034009]
- Fundamental Research Funds for the Central Universities [N130618001]
A steel containing Fe-0.20C-1.57Mn-1.55Si-0.0029P-0.0018S (wt%) was treated by quenching and partitioning (Q&P) and quenching and tempering (Q&T) process. The resulted mechanical properties indicate that the Q&P process may bring on an excellent combination of strength and elongation for the steel, of which the product was between 14.5 and 20.4 GPa%. The morphological relationship between the retained austenite and martensite was characterized as well. It was found that the TRIP effect of retained austenite plays an important role in enhancing the work hardening rate and instantaneous n-value at high strain level, which further increases the uniform elongation. Fractography of samples treated by Q&P process showed mainly ductile mechanism, while a small percentage of brittle fracture exists in the samples treated by Q&T process. Possible isothermal decomposition of austenite at quenching temperature (QT) and partitioning temperature (PT) and its effect on carbon partitioning was discussed. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据