MATERIALS LETTERS
卷 144, 期 -, 页码 74-77出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.matlet.2014.12.082
关键词
Ceramic membrane; Alumina support; Porous materials; Corrosion
资金
- National Natural Science Foundation of China [51472092]
- Industry, Education and Academy Cooperation Project of Foshan City, Guangdong Province [2012HC100282]
An ultra-high purity porous alumina ceramic support was prepared by boehmite-coated alumina powders at a relatively low temperature. Its corrosion resistance in 20 wt% H2SO4 and 10 wt% NaOH hot solutions for 2 to 8 h was investigated. After corrosion in H2SO4 solution for 8 h, the mass loss was only 0.55%, the flexural strength decreased by 9.85% and the open porosity increased from 41.14% to 47.25%. Meanwhile, the average pore diameter increased from 1.22 mu m to 1.60 mu m. While in NaOH solution for 8 h, the mass of the support and the flexural strength were diminished by 0.48% and 8.08%, the open porosity and the average pore size were increased to 46.48% and 1.49 mu m. The permeability increases from 7.18 x 10(-10) m(2) to 1.35 x 10(-9) m(2) and 1.25 x 10(-9) m(2), respectively, after acidic and alkaline corrosion for 8 h. The support shows an excellent corrosion resistance. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据