期刊
MATERIALS CHEMISTRY AND PHYSICS
卷 162, 期 -, 页码 346-353出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.matchemphys.2015.05.077
关键词
Two-step surface modification; Sodium silicate; Ambient pressure drying; Fiber reinforced; Shape-controllable; Thermal conductivity
资金
- National Natural Science Foundation of China [11372263]
The shape-controllable sodium silicate based fiber reinforced silica aerogel monoliths with excellent integrity and thermal insulating property were prepared by ambient pressure drying. The non-woven silica fiber up to 17.5 wt% could be uniformly distributed and well incorporated into the three-dimensional silica network since the fiber introduced and silica precursor could simultaneously react with methyltriethoxysilane (MTES) and trimethylchlorosilane (TMCS) during the two-step surface modification. The densities and porosities of the composite silica aerogel monoliths were 0.104-0.146 g/cm(3) and 93%-95%, respectively, with the thermal conductivities of 21-31 m W/(m K) and the average modulus of 323-535 kPa. The characteristic linear and zigzag responses were observed from the compression stress strain curves. Incomplete modification due to a large amount of fiber incorporation led to severe volume shrinkage during ambient pressure drying. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据