Microstructural, mechanical and electrochemical behaviour of a 7017 Al-Zn-Mg alloy of different tempers

The aim of the investigation is to assess the microstructural features and associated physical, mechanical and electrochemical properties of a 7017 Al-Zn-Mg alloy of various tempers. A 7017 Al-Zn-Mg alloy was subjected to different ageing schedules to produce under-(T4), peak-(T6), over-(T7) and highly over-aged tempers. Optical microscopy, hardness measurement, electrical conductivity measurement, tensile testing and SEM fractographs, differential scanning calorimetry (DSC), transmission electron microscopy (TEM), and electrochemical polarization studies have been used to characterize the alloy tempers. Hardness measurement and tensile testing showed the characteristic age hardening phenomenon of aluminium alloys. Optical and TEM micrographs have revealed the variation in size of matrix strengthening eta (MgZn2) and also the size and distribution of grain boundary eta (MgZn2) precipitate with ageing time. DSC thermograms exhibiting exothermic and endothermic peaks indicated the characteristic solid state reaction sequence of the 7017 alloy. Potentiodynamic polarization study of the 7017 alloy of various tempers in 3.5 wt.% NaCl solution at near neutral pH showed typical active metal dissolution behaviour, but at pH 12 an active-passive-transpassive transition behaviour has been observed. (C) 2015 Elsevier Inc. All rights reserved.