Nano-omposite; epoxy; nano-micro-composite; nano-Al2O3; surface discharge; PD resistance; erosion; breakdown strength
资金
- MEX of Japan Regional Innovation Cluster Initiative [23-2]
- National Nature Science Foundation of China (NSFC) [NSFC: 51007057]
Epoxy composite is expected to become the substrate insulation of gate bipolar transistors (IGBTs) that can replace ceramics if it has high thermal conductivity. Fillers with high thermal conductivity were added to the epoxy resin, while this composite often suffers from lowering in breakdown (BD) strength. In order to reveal the above phenomena and to clarify the breakdown (BD) mechanism, we carried out experiments using several electrode structures, i.e. an MB-PWB (metal-base printed wiring board) insulation simulated structure, a rod-to-plane electrode for PD erosion resistance, and a sphere-to-sphere electrode for BD strength. As a result, it was clarified that the IGBT insulation breaks down after successive partial discharges (PDs), and the BD strength of microcomposite decreases with increasing the content of micro-fillers, while PD resistance of microcomposite is improved with increasing the content of micro-fillers. A trial was made to raise the once-lowered BD strength by adding nano-Al2O3 fillers. Above experiments were carried out for nanocomposites and nano-micro-composites. It was clarified that the nano-fillers can improve the PD resistance of composites obviously, while nano-fillers improve the BD strength of composite slightly. Such a phenomenon was found that the BD strength of composites was increased with the dispersion state of nano-fillers.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据