IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY
卷 21, 期 3, 页码 2858-2861出版社
IEEE-INST ELECTRICAL ELECTRONICS ENGINEERS INC
DOI: 10.1109/TASC.2010.2086031
关键词
Critical current density; critical temperature; FeTe0.5Se0.5; superconducting wires
资金
- Japan Society for the Promotion of Science [22-10227]
- KAKENHI
FeTe0.5Se0.5 superconducting wires have been fabricated using ex-situ PIT method with an Fe sheath. Among the other FeAs-based superconductors, FeTe0.5Se0.5 has great advantage for applications due to its binary composition and less toxicity. Surprisingly, superconducting current was observed in the as-fabricated wire without any heat treatments. The zero-resistivity critical temperature (T-c(zero)) and transport critical current density (J(c)) at 2K were 3.2 K and 2.8 A/cm(2), respectively. In addition, by annealing at 200 degrees C for 2 h, T-c(zero) and J(c) were enhanced up to 9.1 K, and 64.1 A/cm(2), respectively. This suggests that the inter-grain connectivity was improved by heat treatment, and superconducting properties of FeTe0.5Se0.5 wire were enhanced.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据