IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY
卷 21, 期 3, 页码 2878-2881出版社
IEEE-INST ELECTRICAL ELECTRONICS ENGINEERS INC
DOI: 10.1109/TASC.2010.2079311
关键词
Addition; Ag sheath; critical current; grain connectivity; iron pnictides; wires and tapes
资金
- Beijing Municipal Science and Technology Commission [Z09010300820907]
- National '973' Program [2011CB605905]
The development of PIT fabrication process of iron pnictide superconducting wires and tapes has been reviewed. Silver was found to be the best sheath material, since no reaction layer was observed between the silver sheath and the superconducting core. The grain connectivity of iron pnictide wires and tapes has been markedly improved by employing Ag or Pb as dopants. At present, critical current densities in excess of 3750 A/cm(2) (I-c = 37.5 A) at 4.2 K have been achieved in Ag-sheathed SrKFeAs wires prepared with the above techniques, which is the highest value obtained in iron-based wires and tapes so far. Moreover, Ag-sheathed Sm-1111 superconducting tapes were successfully prepared by PIT method at temperatures as low as similar to 900 degrees C, instead of commonly used temperatures of similar to 1200 degrees C. These results demonstrate the feasibility of producing superconducting pnictide composite wires, even grain boundary properties require much more attention.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据