Direct Applicability of La0.6Sr0.4CoO3 - δ Thin Film Cathode to Yttria Stabilised Zirconia Electrolytes at T ≤ 650 °C

Journal

FUEL CELLS
Volume 10, Issue 6, Pages 1057-1065

Publisher

WILEY-V C H VERLAG GMBH
DOI: 10.1002/fuce.201000009

Keywords

Lanthanum Strontium Cobalt Oxide (LSC); Micro-Solid Oxide Fuel Cells (Micro-SOFCs); Pulsed Laser Deposition (PLD); Thin Film Cathodes

Funding

  1. Korea Institute of Science and Technology (KIST)
  2. Seoul RBD program [CS070157]

Ask authors/readers for more resources

For investigating the direct applicability of highly active cobalt containing cathodes on YSZ electrolytes at a lower processing and operating temperature range (T <= 650 degrees C), we fabricated a thin film lanthanum strontium cobalt oxide (LSC) cathode on an yttria stabilised zirconia (YSZ)-based solid oxide fuel cell (SOFC) via pulsed laser deposition (PLD). Its electrochemical performance (5.9 mW cm(-2) at 0.7 V, 650 degrees C) was significantly inferior to that (595 mW cm(-2) at 0.7 V, 650 degrees C) of an SOFC with a thin (t similar to 200 nm) gadolinium doped ceria (GDC) buffer layer in between the LSC thin film cathode and the YSZ electrolyte. It implies that even though the cathode processing and cell operating temperatures were strictly controlled not to exceed 650 degrees C, the direct application of LSC on YSZ should be avoided. The origin of the cell performance deterioration is thoroughly studied by glancing angle X-ray diffraction (GAXRD) and transmission electron microscopy (TEM), and the decomposition of the cathode and diffusion of La and Sr into YSZ were observed when LSC directly contacted YSZ.

Authors

I am an author on this paper
Click your name to claim this paper and add it to your profile.

Reviews

Primary Rating

4.4
Not enough ratings

Secondary Ratings

Novelty
-
Significance
-
Scientific rigor
-
Rate this paper

Recommended

No Data Available
No Data Available