Journal
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
Volume 35, Issue 10, Pages 2895-2906Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2015.03.036
Keywords
Transparent YAG; Titanium; Wetting; Interface structure; Metal-ceramic joining
Categories
Funding
- Flagship CNR-MIUR project RITMARE, Research Unit [SP1-WP5-AZ1-UO09]
Ask authors/readers for more resources
The wetting of transparent YAG (Y3Al5O12) by alloys of the AgCuTi system has been studied for the first time. The role of the activity of Ti in determining the interactions between the brazing alloys and the YAG substrate has been analyzed by CALPHAD method. The low contact angle values ensure very good (at 950 degrees C) and fair (at 850 degrees C and 820 degrees C) wettability conditions. A significant reactivity occurred at the solid liquid interfaces, with the formation of new phases. TiY2O5 was found at Ag-Ti/YAG interfaces, while a second layer, identified as M4X, associated to the significant wettability improvement, was specifically found only in the AgCuTi/YAG samples tested at 950 degrees C. All these phases were identified by the newly calculated Ag-Cu-Ti phase diagram and were confirmed by SEM and EDS analyses. The obtained good wettability and the maintained transparency of the YAG are promising for the production of brazed optical windows to be used under extreme conditions. (C) 2015 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available